This thesis summarizes the development and characterization of novel hydrogels based on polymerized ionic liquids. Next to the thermal properties of these materials, the mechanical characterization by tensile and compression tests was mainly performed using various parameters influencing the stability. In addition, a comparison with well-known hydrogels was made. These materials were used as artificial vessel model to carry out balloon dilations. By use of a flow-through cell, an artificial vessel wall could be generated. The drug release of drug-coated balloon catheters as the first and important phase was characterized in detail. The drug delivery as well as the transfer into the vessel wall was investigated for different hydrogels and compared to each other.
Diese Arbeit befasst sich mit der Entwicklung und Charakterisierung von neuartigen Hydrogelen auf Basis von polymerisierten ionischen Flüssigkeiten. Neben den thermischen Eigenschaften dieser Materialien wurde im Hauptteil dieser Arbeit die mechanische Charakterisierung durch Zug- und Druckversuche vorgenommen, wobei verschiedene Einflussparameter auf die Stabilität untersucht wurden. Außerdem erfolgte ein Vergleich mit bereits bekannten Hydrogelen. Die Materialien wurden als künstliches Gewebemodell eingesetzt, um Ballondilatationen vorzunehmen. Mit Hilfe einer Durchflusszelle konnte eine Gefäßwand künstlich erzeugt werden. Die Wirkstoffverteilung von beschichteten Ballonkathetern konnte in der ersten wichtigen Phase der Freisetzung charakterisiert werden. Die Wirkstoffabgabe sowie der Transport in die Gefäßwand wurden für verschiedene Hydrogele untersucht und miteinander verglichen.